Sterling Silver "88" is a proprietary deoxidized sterling silver
designed to eliminate fire scale and porosity. Sterling Silver "88"
will be slightly softer than standard sterling silver, while still
retaining the advantageous characteristics of our other sterling
silver grains.
Melting: Traditional methods of melting regular sterling silver
I.E. (as cool as possible) will cause a variety of problems. Most
failures with these sterling products are caused by too low of a
melt temperature. Customers familiar with silicon deoxidized gold
casting alloys should have less trouble adjusting to the appearance
of these silvers.
MELTING
Temperature Range 980° - 1000° C.
1796° - 1832° F.
REMELTING
We recommend a 50% fresh mix. Our sterling silver replenisher can
also be used without adding fresh.
FLUXING
It may be necessary to flux these silver melts. We recommend Boric
Acid. Do not use Carbon Containing Fluxes or Charcoal. Skim any
surface oxides off the surface before stirring.
QUENCH TIME
15 - 20 minutes.
HARDNESS AND HEAT TREATMENT
It can be hardened further by heat treatment at 300°C / 575° F for 1
hour, and air cool.
INVESTMENT REMOVAL
Most standard investment removers will successfully remove the
investment powder. The best solutions are the sulfuric and
hydrofluoric based products. UNITED's Brite-Cast Investment Remover
also works well, although it is less aggressive and will take
longer.
FLASK TEMPERATURE
Use your regular flask temperatures.
FIRE SCALE
Fire scale is completely eliminated.