 #970
Alloy
Thank you for using UNITED'S alloys.
UNITED'S #970 ALLOY may be used for 10K & 14K white gold casting,
which produces an off- white finished color. #970 contains silicon,
and boron deoxidizers.
You should obtain excellent results by following a few simple
instructions.
MELTING
| Melt Temperature for 10k Alloyed Grain |
1010°- 1020°C |
1850°-1868°F |
| Melt Temperature for 14k Alloyed Grain |
980°- 990°C |
1796°-1814°F |
| Melt Temperature for Alloying |
1040°- 1050°C |
1904°- 1922°F |
We do recommend pre-graining all alloy and fine gold before
casting to assure a uniform mixture.
FLASK TEMPERATURE
We suggest a slightly higher flask temperature for white gold.
FLUXING
Fluxing white gold is extremely important to pick-up oxides. Boric
Acid is the recommended flux. Do not use carbon fluxes or any fluxes
designed for refining; i.e. soda ash, saltpeter, etc. Avoid flux in
bottom pour automatic casting units.
QUENCH TIME
15 minutes
INVESTMENT REMOVAL
Most standard investment removers will successfully remove the
investment powder. Fluoric-based investment removers are the best
for removing the silicon oxide invisible coating. UNITED'S Brite-Cast
Investment Remover also works very well.
REMELTING
We recommend a 70% fresh - 30% scrap mix. White gold alloy has about
1/3 the reusability of yellow gold alloys.
NOTES
Melt temperature may vary with type of unit. This alloy is designed
for casting only.