 #392
Alloy
Thank you for using UNITED'S alloys.
UNITED'S 392 ALLOY is designed for 18K - 22K yellow gold casting,
which produces a light yellow color in 18K, and a medium yellow
color in 20K - 22K.
You should obtain excellent results by following a few simple
instructions.
MELTING
| Melt Temperature for 18K Alloyed Grain |
1020°- 1030°C |
1868°-1886°F |
| Melt Temperature for 20K - 22K Alloyed Grain |
1100° - 1130°C |
2012° - 2066°F |
| Melt Temperature for Alloying 18K |
1070°- 1080°C |
1958°- 1976°F |
| Melt Temperature for Alloying 20K - 22K |
1080°- 1100°C |
1976°- 2012°F |
We do recommend pre-graining all alloy and fine gold before
casting to assure a uniform mixture.
FLASK TEMPERATURE
| For 18K |
use normal recommended temperature |
| For 20K-22K Vacuum casting |
676° - 730° C |
1250° - 1350° F |
| For 20K-22K Centrifugal casting |
537° - 565° C |
1000° - 1050° F |
FLUXING
Boric Acid is the recommended flux. Use as little flux as possible.
Do not use carbon fluxes or any fluxes designed for refining; i.e.
soda ash, saltpeter, etc. Avoid flux in bottom pour automatic
casting units.
QUENCH TIME
15 - 20 minutes
INVESTMENT REMOVAL
Most standard investment removers will successfully remove the
investment powder. Fluoric-based investment removers are the best
for removing the silicon oxide invisible coating. UNITED'S Brite-Cast
Investment Remover also works very well.
REMELTING
We recommend a 50% rejuvenation for remelting.
NOTES
Melt temperature may vary with type of unit. This alloy is
designed for casting only.